MITIS CASTING
\mˈa͡ɪtɪs kˈastɪŋ], \mˈaɪtɪs kˈastɪŋ], \m_ˈaɪ_t_ɪ_s k_ˈa_s_t_ɪ_ŋ]\
Definitions of MITIS CASTING
Sort: Oldest first
-
A process, invented by P. Ostberg, for producing malleable iron castings by melting wrought iron, to which from 0.05 to 0.1 per cent of aluminium is added to lower the melting point, usually in a petroleum furnace, keeping the molten metal at the bubbling point until it becomes quiet, and then pouring the molten metal into a mold lined with a special mixture consisting essentially of molasses and ground burnt fire clay; also, a casting made by this process; -- called also wrought-iron casting.
By Oddity Software
-
A process, invented by P. Ostberg, for producing malleable iron castings by melting wrought iron, to which from 0.05 to 0.1 per cent of aluminium is added to lower the melting point, usually in a petroleum furnace, keeping the molten metal at the bubbling point until it becomes quiet, and then pouring the molten metal into a mold lined with a special mixture consisting essentially of molasses and ground burnt fire clay; also, a casting made by this process; -- called also wrought-iron casting.
By Noah Webster.
Word of the day
Proto Oncogene Proteins c erbB 2
- cell surface protein-tyrosine kinase that is found to be overexpressed in significant number adenocarcinomas. It has extensive homology can heterodimerize EGF EPIDERMAL GROWTH FACTOR), 3 receptor (RECEPTOR, 3) and the 4 receptor. Activation of erbB-2 receptor occurs during heterodimer formation with a ligand-bound erbB family members. EC 2.7.11.-.